Tensile bond strength of silicone-based soft denture liner to two chemically different denture base resins after various surface treatments


Akin H., TUĞUT F., Guney U., KIRMALI Ö., Akar T.

LASERS IN MEDICAL SCIENCE, cilt.28, sa.1, ss.119-123, 2013 (SCI-Expanded) identifier identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 28 Sayı: 1
  • Basım Tarihi: 2013
  • Doi Numarası: 10.1007/s10103-012-1082-7
  • Dergi Adı: LASERS IN MEDICAL SCIENCE
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.119-123
  • Anahtar Kelimeler: PMMA, UDMA, Eclipse, Soft liner, Er:YAG laser, Tensile bond strength, LINING MATERIALS, RELINING MATERIALS, ADHESION, POLYMERS, HARDNESS
  • Akdeniz Üniversitesi Adresli: Evet

Özet

This study evaluated the effect of various surface treatments on the tensile bond strength of a silicone-based soft denture liner to two chemically different denture base resins, heat-cured polymethyl methacrylate (PMMA), and light-activated urethane dimethacrylate or Eclipse denture base resin. PMMA test specimens were fabricated and relined with a silicone-based soft denture liner (group AC). Eclipse test specimens were prepared according to the manufacturer's recommendation. Before they were relined with a silicone-based soft denture liner, each received one of three surface treatments: untreated (control, group EC), Eclipse bonding agent applied (group EB), and laser-irradiated (group EL). Tensile bond strength tests (crosshead speed = 5 mm/min) were performed for all specimens, and the results were analyzed using the analysis of variance followed by Tukey's test (p = 0.05). Eclipse denture base and PMMA resins presented similar bond strengths to the silicone-based soft denture liner. The highest mean force was observed in group EL specimens, and the tensile bond strengths in group EL were significantly different (p < 0.05) from those in the other groups.