Structural, Optical and Magnetic Properties of alpha-Fe2O3-SiO2 and Dy2O3-SiO2 Composites Produced by a Facile Method


Creative Commons License

Kendir E., Tekgul A., KÜÇÜK İ., Yaltkaya S.

JOURNAL OF ELECTRONIC MATERIALS, cilt.49, sa.1, ss.798-806, 2020 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 49 Sayı: 1
  • Basım Tarihi: 2020
  • Doi Numarası: 10.1007/s11664-019-07718-1
  • Dergi Adı: JOURNAL OF ELECTRONIC MATERIALS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, PASCAL, Applied Science & Technology Source, Chemical Abstracts Core, Chimica, Compendex, Computer & Applied Sciences, INSPEC
  • Sayfa Sayıları: ss.798-806
  • Anahtar Kelimeler: Silica, Fe2O3-SiO2, Dy2O3-SiO2, optical properties, PHOTOCATALYTIC DEGRADATION, NANOPARTICLES, NANOSTRUCTURES, LANTHANUM, GLASSES, ROUTE, FTIR
  • Akdeniz Üniversitesi Adresli: Evet

Özet

We prepared SiO2, Fe2O3-SiO2, and Dy2O3-SiO2 composites by an enhanced method and reported the result of their structural, optical and magnetic properties. In the x-ray diffraction results of the Fe2O3-SiO2, Fe2O3 and the SiO2 it is evident that these composites are crystallized in rhombohedral and trigonal structures, respectively. In the Dy2O3-SiO2 composite, SiO2 transforms into a trigonal structure with the addition of Dy. The absorption bands belong to Fe2O3, and Dy2O3 were obtained using the Fourier transform infrared spectra. In ultraviolet-visible spectra, the photocatalytic properties of Fe2O3-SiO2 and Dy2O3-SiO2 were determined as a function of time at room temperature. Maximum transmittance change at 800 nm was 75% and 40% for composites Fe2O3-SiO2, and Dy2O3-SiO2, respectively. The photocatalytic property of Dy2O3-SiO2 composite increases gradually from short to long in the wavelength region where it exhibits a maximum value in the visible region. In magnetic measurements, a weak ferromagnetic behavior was observed in the Fe2O3-SiO2, while Dy2O3-SiO2 exhibited paramagnetic behavior as expected. The saturation and coercivity values for Fe2O3-SiO2 were found to be 0.15 Am-2 kg(-1) and 40 mT, respectively.