Coating Effect on Magnetic Properties of Fe36Co36B19.2Si4.8Mo3W1 Amorphous Ribbons


Creative Commons License

Perincek F., HACIİSMAİLOĞLU M. C., Sarlar K., HACIİSMAİLOĞLU M. C., ALPER M., Kucuk I.

ACTA PHYSICA POLONICA A, cilt.125, sa.2, ss.408-410, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 125 Sayı: 2
  • Basım Tarihi: 2014
  • Doi Numarası: 10.12693/aphyspola.125.408
  • Dergi Adı: ACTA PHYSICA POLONICA A
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.408-410
  • Akdeniz Üniversitesi Adresli: Evet

Özet

In this research, the electrodeposition technique was employed to prepare fine-grained nickel, iron and iron-cobalt coatings with 1 pm thicknesses on the substrate of the Fe36Co36B19.2Si4.8Mo3W1 amorphous ribbons. The coating effect on magnetic properties was examined at room temperature using an ADE Magnetics EV9 vibrating sample magnetometer with maximum magnetic field strength of 1750 kA/m. It is found that Ni, Fe, and Fe-Co coated amorphous ribbons show 0.60, 0.71, and 1.01 T saturation magnetization, respectively, while uncoated ribbon has 1.55 T.